Shincolon‑III continuous silicon carbide fibers are prepared using electron-beam‑assisted crosslinking in an active atmosphere combined with high‑temperature decarbonization heat treatment

Category:

Shincolon-Ⅲ type continuous silicon carbide fiber

message
Product

Phone:86-574-88951579

Email: zxxc@nbzxxc.cn

Product Description

Shincolon‑III continuous silicon carbide fibers are prepared using electron-beam‑assisted crosslinking in an active atmosphere combined with high‑temperature decarbonization heat treatment. This fiber grade has an oxygen content of less than 0.8 wt% and a carbon-to-silicon ratio of approximately 1.05. It can be used continuously at temperatures below 1600°C in an oxygen‑free environment and below 1350°C in an oxygen‑containing environment.

GradeTow (K)Diameter (μm)Carbon-to-silicon ratioStrength (GPa)Modulus (GPa) Oxygen content (wt%)
Shincolon23290.2 11.5±1.01.05±0.1≥3.0≥350<0.8

Keywords:

Shincolon2309

Related products

Polycarbosilane

Polycarbosilane

Polycarbosilane (PCS) is a polymer with a Si–C backbone that can be converted into silicon carbide ceramics via high-temperature pyrolysis
Zirconium-carbon-silane polymer

Zirconium-carbon-silane polymer

Polyzirconium carbosilane (PZCS) is a novel zirconium‑containing polycarbosilane polymer that can be used to prepare zirconium‑bearing multiphase
Shincolon2158

Shincolon2158

Shincolon‑I type continuous silicon carbide fibers are prepared using an electron‑beam‑assisted air crosslinking technique
Shincolon2108

Shincolon2108

Shincolon‑I type continuous silicon carbide fiber is a silicon carbide fiber prepared using an electron‑beam‑assisted air crosslinking technique