Shincolon2259

Shincolon‑II continuous silicon carbide fibers are prepared using an electron-beam‑assisted crosslinking technique in an active atmosphere

Category:

Shincolon-II type continuous silicon carbide fiber

message
Product

Phone:86-574-88951579

Email: zxxc@nbzxxc.cn

Product Description

Shincolon‑II continuous silicon carbide fibers are prepared using an electron-beam‑assisted crosslinking technique in an active atmosphere. Owing to the carbon‑rich precursor and oxygen‑free crosslinking conditions, these fibers exhibit an oxygen content of less than 1 wt% and a carbon-to-silicon ratio of at least 1.3. They can be used continuously at temperatures below 1400°C in an oxygen‑free environment and below 1250°C in an oxygen‑containing environment.

GradeTow (K)Diameter (μm)Carbon-to-silicon ratioStrength (GPa)Modulus (GPa)Oxygen content (wt%)
Shincolon22590.5 13.0±1.0≥1.3≥2.8≥280≤1.0

Keywords:

Shincolon2259

Related products

Polycarbosilane

Polycarbosilane

Polycarbosilane (PCS) is a polymer with a Si–C backbone that can be converted into silicon carbide ceramics via high-temperature pyrolysis
Zirconium-carbon-silane polymer

Zirconium-carbon-silane polymer

Polyzirconium carbosilane (PZCS) is a novel zirconium‑containing polycarbosilane polymer that can be used to prepare zirconium‑bearing multiphase
Shincolon2158

Shincolon2158

Shincolon‑I type continuous silicon carbide fibers are prepared using an electron‑beam‑assisted air crosslinking technique
Shincolon2108

Shincolon2108

Shincolon‑I type continuous silicon carbide fiber is a silicon carbide fiber prepared using an electron‑beam‑assisted air crosslinking technique